✨ New Arrivals Just Dropped!Explore
HomeStore

ARCCAPTAIN Aluminum Welding Wire 1 Pound Aluminum MIG Wire

Product image 1
Product image 2
Product image 3
Product image 4
Product image 5
Product image 6
Product image 7
Product image 8
Product image 9
Product image 10
Product image 11
Product image 12
Product image 13
Product image 14
Product image 15
Product image 16
Product image 17
Product image 18
Product image 19
Product image 20

ARCCAPTAIN Aluminum Welding Wire 1 Pound Aluminum MIG Wire

ARCCAPTAIN ER4043 ER5356 Aluminum Wire Guide
Performance Characteristics The differing chemical compositions lead to distinct performance characteristics:
  • Strength ER5356 is significantly stronger, with a typical shear strength of 18 KSI compared to 11 KSI for ER4043. It is the standard for load-bearing structural parts.
  • Operating Temperature ER4043 can be used in environments exceeding 150°F (66°C), while ER5356 is not recommended for these elevated temperatures due to potential stress corrosion cracking.
  • Ductility ER5356 is more ductile and flexible, making it better for parts subject to vibration or post-weld forming.
  • Anodizing Color Match ER5356 provides a much better color match to the base metal after anodizing. ER4043 typically turns dark gray or black after the process.
Welding Performance & Ease of Use The two fillers behave differently during the welding process:
  • Weldability & Flow ER4043 has excellent fluidity and a lower melting point, making it easier for beginners to control and better at bridging gaps.
  • Wire Feeding Because it is stiffer, ER5356 often feeds more reliably through MIG welding systems. ER4043 is softer and more prone to feeding issues without a spool gun.
  • Crack Resistance ER4043 is highly resistant to hot cracking, especially when welding 6xxx series alloys like 6061.
  • Aesthetics ER4043 produces smoother, shinier welds with less spatter. ER5356 welds often have a duller, "frosty" appearance and generate more soot (smut).
Common Applications
Application Recommended Filler Reason
Marine / Saltwater ER5356 Superior corrosion resistance.
6061-T6 Base Metal Either Choice depends on strength vs. ease.
Aluminum Castings ER4043 Excellent crack resistance and low porosity.
Pressure Vessels ER5356 High structural integrity requirements.
Automotive Radiators ER4043 Good flow on thin materials, high temp tolerance.
Chemical Composition Comparison Standard Reference: AWS A5.10 / ISO 18273
Composition Elements 4043 (AlSi5) 5356 (AlMg5)
Silicon (Si) 4.5 – 6.0% ≤ 0.25%
Magnesium (Mg) — 4.5 – 5.5%
Manganese (Mn) — 0.05 – 0.20%
Iron (Fe) ≤ 0.8% ≤ 0.4%
Copper (Cu) ≤ 0.3% ≤ 0.1%
Zinc (Zn) ≤ 0.1% ≤ 0.25%
Titanium (Ti) ≤ 0.2% ≤ 0.2%
Other Impurities ≤ 0.15% ≤ 0.15%
Aluminum (Al) Balance Balance
Product Images
Aluminum Welding Wire Aluminum Welding Wire 1 Aluminum Welding Wire 2 Aluminum Welding Wire 3 Aluminum Welding Wire 4 ER5356 0.035 Aluminum Welding Wire ER5356 0.035 Aluminum Welding Wire ER5356 0.035 Aluminum Welding Wire
Select Size
From $5.60

Original: $15.99

-65%
ARCCAPTAIN Aluminum Welding Wire 1 Pound Aluminum MIG Wire—

$15.99

$5.60

Product Information

Shipping & Returns

Description

ARCCAPTAIN ER4043 ER5356 Aluminum Wire Guide
Performance Characteristics The differing chemical compositions lead to distinct performance characteristics:
  • Strength ER5356 is significantly stronger, with a typical shear strength of 18 KSI compared to 11 KSI for ER4043. It is the standard for load-bearing structural parts.
  • Operating Temperature ER4043 can be used in environments exceeding 150°F (66°C), while ER5356 is not recommended for these elevated temperatures due to potential stress corrosion cracking.
  • Ductility ER5356 is more ductile and flexible, making it better for parts subject to vibration or post-weld forming.
  • Anodizing Color Match ER5356 provides a much better color match to the base metal after anodizing. ER4043 typically turns dark gray or black after the process.
Welding Performance & Ease of Use The two fillers behave differently during the welding process:
  • Weldability & Flow ER4043 has excellent fluidity and a lower melting point, making it easier for beginners to control and better at bridging gaps.
  • Wire Feeding Because it is stiffer, ER5356 often feeds more reliably through MIG welding systems. ER4043 is softer and more prone to feeding issues without a spool gun.
  • Crack Resistance ER4043 is highly resistant to hot cracking, especially when welding 6xxx series alloys like 6061.
  • Aesthetics ER4043 produces smoother, shinier welds with less spatter. ER5356 welds often have a duller, "frosty" appearance and generate more soot (smut).
Common Applications
Application Recommended Filler Reason
Marine / Saltwater ER5356 Superior corrosion resistance.
6061-T6 Base Metal Either Choice depends on strength vs. ease.
Aluminum Castings ER4043 Excellent crack resistance and low porosity.
Pressure Vessels ER5356 High structural integrity requirements.
Automotive Radiators ER4043 Good flow on thin materials, high temp tolerance.
Chemical Composition Comparison Standard Reference: AWS A5.10 / ISO 18273
Composition Elements 4043 (AlSi5) 5356 (AlMg5)
Silicon (Si) 4.5 – 6.0% ≤ 0.25%
Magnesium (Mg) — 4.5 – 5.5%
Manganese (Mn) — 0.05 – 0.20%
Iron (Fe) ≤ 0.8% ≤ 0.4%
Copper (Cu) ≤ 0.3% ≤ 0.1%
Zinc (Zn) ≤ 0.1% ≤ 0.25%
Titanium (Ti) ≤ 0.2% ≤ 0.2%
Other Impurities ≤ 0.15% ≤ 0.15%
Aluminum (Al) Balance Balance